牌号简介 About |
---|
SABIC® HDPE B5429是一种中分子量高密度聚乙烯共聚物。它通常用于吹塑小尺寸的瓶子。SABIC® HDPE B5429具有很好的韧性、抗应力开裂性(ESCR)、承载强度和加工性能。典型应用。SABIC® HDPE B5429属于多用途吹塑等级。它可以吹塑成家用和工业化学品(如洗涤剂、漂白剂、织物柔软剂、溶剂、油漆等)、汽车用品、食品、洗漱用品和化妆品的容器。它通常也用于其他空心薄壁零件和型材挤压。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® HDPE B5429 is a medium molecular weight high density polyethylene copolymer. It is typically used for blow moulding bottles of small sizes. SABIC® HDPE B5429 offers a very good combination of toughness, stress cracking resistance (ESCR), load bearing strength and processability characteristics. Typical applications. SABIC® HDPE B5429 is classified as a multipurpose blow moulding grade. It may be blow moulded into containers for household and industrial chemicals (e.g. detergents, bleach, fabric softeners, solvents, paints, etc.), automotive supplies, foodstuffs, toiletries and cosmetics. It is typically also used for other hollow thin-walled parts and profile extrusions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.954 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.30 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
29 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
1.5 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,模压成型,F50 10% non-ionic detergent, molded, F50 |
40.0 | hr | ASTM D1693B |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,模压成型 -30 ℃, molded |
kJ/m² | ISO 180-A | |
23℃,模压成型 23 ℃, molded |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
熔融温度 Melting temperature |
℃ | DIN 53765 | |
Enthalpy Change Enthalpy Change |
J/g | DIN 53765 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow Molding Melt Temperature Blow Molding Melt Temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
拉伸应变 Tensile strain |
|||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
国外限制塑料制品的做法
2017-06-30 对环保的重视,应该涉及到生活的各个方面。记者认为,要加强宣传,多进行科普教育,培养大家的环保意识,并形成良性循环。来看看其他国家的做法。 押金借用 目前在一部分发达国家中采取了押金制度。以德国为例,超市中的矿泉水瓶子都有一个回收价格,顾客在喝完之后可以前往指定地点的回收机器,可以获得回收押金。在国内,押金制实施也曾有过成功案例。上海市在2000年就颁布实施了《一次性塑料饭盒管理暂行办法》,在一次性塑料饭盒回收过程中成功推行了押金制。 优惠鼓励 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |