牌号简介 About |
---|
utomer TPU,包括酯型和醚型。适用于鞋服人造革压延、挤出,与PVC复合。 Utomer TPU which include ester and ether type. It's suitable for calendering and extrusion, which are used for shoes and clothing leatherette and compounding with PVC. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
4.00 | MPa | ASTM D412 |
300% 应变 300% strain |
7.00 | MPa | ASTM D412 |
拉伸强度 tensile strength |
30.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
800 | % | ASTM D412 |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
磨损量 Wear amount |
mm³ | DIN 53516 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
新3D网格技术大幅缩短塑件充填模拟前处理时间
2017-10-20 3D流道网格技术的产生为塑料充填模拟提供了更多的方法与可能。新一代的3D网格技术将大幅缩短模拟前处理时间。 过去在塑件充填模拟的技术发展过程中,多着重于产品本身的充填过程。在分析流道时,常会用1D线架构及简化的数值假设,求得熔胶在模腔中由流道末端进入产品时的流速、压力等数值,作为模拟塑件充填的入口条件。 后来随着流道的模拟渐渐受到重视,进而导入3D流道网格技术,将充填模拟提前到流道的起始端,模拟出熔胶在流道中的各种流动行为以 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |