牌号简介 About |
---|
MF5000是采用CSTR浆体工艺技术生产的篷布用扁纱。MF5000非常适合用于单丝应用。MF5000具有良好的拉伸、旋压、高强度和熔融稳定性。钢丝绳、网等用单丝。 MF5000 is manufactured to be processed in flat yarn for tarpaulin by CSTR Slurry process technology. MF5000 is ideally suited for use in monofilament application. MF5000 offers good stretching, spinning, high strength property and melting stability. Application Monofilament for Rope and Net, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.951 到 0.956 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 到 1.1 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
> 98 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
> 50.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
> 120 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
我国复合膜减薄部分研讨达国际程度
2016-03-01 复合膜减薄技术是指在确保复合膜满足保护内容物、方便携带和促进销售等功能的条件下,通过采用一系列有效措施,如材料改性、材料选择、材料多功能化、材料结构优化以及工艺技术创新等,使用最少量的材料进行适度包装。 我国在复合膜减薄方面的研究也取得了较大进展,部分已经达到国际先进水平。 复合膜减薄技术不仅可以减少生产过程的材料用量,节省资源和能源,降低生产和运输成本,有助于企业实现更好的盈利,而且能减少包装废弃物产生量,降低VOCs排放,减少回收再利用费用,是实现生态保 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |