牌号简介 About |
---|
WELLAMID Nylon 6600 PA-66-HWL是一种聚酰胺66(尼龙66)材料,。 该产品在欧洲有供货,。 WELLAMID Nylon 6600 PA-66-HWL的主要特性有: 阻燃/额定火焰 Flame Retardant 热稳定剂 WELLAMID Nylon 6600 PA-66-HWL的典型应用领域为:汽车行业 WELLAMID Nylon 6600 PA-66-HWL is a Polyamide 66 (Nylon 66) material. It is available in Europe. Important attributes of WELLAMID Nylon 6600 PA-66-HWL are: Flame Rated Flame Retardant Heat Stabilizer Typical application of WELLAMID Nylon 6600 PA-66-HWL: Automotive |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应力 Tensile Stress Tensile Stress |
|||
屈服 yld Yield yld |
85 | MPa | ISO 527 |
拉伸应变 Tensile Strain Tensile Strain |
|||
屈服 yld Yield yld |
60 | % | ISO 527 |
断裂 brk,干燥 dry Broken BRK, dry dry |
4 | % | ISO 527 |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
20 | % | ISO 527 |
拉伸强度 Tensile Strength Tensile Strength |
|||
干燥 dry Dry |
15 | MPa | ISO 527-2 |
湿润 cond. Wet Cond |
MPa | ISO 527-2 | |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
干燥 dry Dry |
MPa | ISO 527 | |
湿润 cond. Wet Cond |
MPa | ISO 527 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179 | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179 | |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179 | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature Melting temperature |
℃ | ||
热变形温度 HDT Hot deformation temperature HDT |
|||
A A |
℃ | ISO 75-1/-2 | |
B B |
℃ | ISO 75-1/-2 | |
维卡软化点 vicat softening point Vicat softening point |
℃ | ISO 306 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
23-80℃ 23-80℃ |
×10-4/K | DIN 53752 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative Permittivity Relative permittivity |
|||
干燥 dry Dry |
1 MHz | IEC 250 | |
湿润 cond. Wet Cond |
1 MHz | IEC 250 | |
耗散因数 Dissipation Factor Dissipation Factor |
|||
干燥 dry Dry |
10-4 | IEC 250 | |
湿润 cond. Wet Cond |
10-4 | IEC 250 | |
耐电强度 Electric strength Electric strength |
|||
干燥 dry Dry |
kV/mm | IEC 243-1 | |
湿润 cond. Wet Cond |
kV/mm | IEC 243-1 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
干燥 dry Dry |
IEC 112 | ||
湿润 cond. Wet Cond |
IEC 112 | ||
体积电阻率 Volume Resistivity Volume Resistance |
|||
干燥 dry Dry |
ohm·cm | IEC 93 | |
湿润 cond. Wet Cond |
ohm·cm | IEC 93 | |
表面电阻率 Surface Resistivity Surface Resistivity |
|||
干燥 dry Dry |
ohm | ISO 3915 | |
湿润 cond. Wet Cond |
ohm | ISO 3915 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
成型收缩率 Molding Shrinkage Molding shrinkage |
% | ||
saturation value at saturation value at |
% | DIN 53495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
0.8 mm,干燥 dry 0.8 mm, dry |
UL 94 | ||
0.8 mm,湿润 cond. 0.8 mm, moist cond |
UL 94 | ||
1.6 mm,干燥 dry 1.6 mm, dry |
UL 94 | ||
1.6 mm,湿润 cond. 1.6 mm, moist cond |
UL 94 | ||
3.2 mm,干燥 dry 3.2 mm, dry |
UL 94 | ||
3.2 mm,湿润 cond. 3.2 mm, wet cond |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
K 2016展前直击:瓦克展现工业用无机硅3D打印机
2016-06-30 瓦克将于K 2016上展示的3D打印机是第一代工业用3D打印机。ACEO Imagine Series K的打印速度明显高于之前的样机,机器结构更为紧凑。 负责瓦克有机硅研发和ACEO团队工作的Bernd Pachaly博士表示:“这台打印机使用了瓦克开发的按需喷墨ACEO技术,它能够制作出至今被视作无法实现的结构复杂的部件或组件。” “增材制造技术”更为通俗的名称叫3D打印。这是一种不借助模具,逐层生产工件的工艺。同常规生产工艺相比,开发人员能够获得更大的 |
K 2016展前直击:瓦克展现工业用无机硅3D打印机 瓦克将于K 2016上展现的三维打印机有第一代工业级三维打印机。ACEO Imagine Series K的打印速率显著高过以前的样品,设备构造更加紧凑型。 承担瓦克有机硅产品研发和ACEO精英团队工作中的Bernd Pachaly博士表明:“这台打印机应用了瓦克开发设计的按需喷墨打印机ACEO技术,它可以制做出迄今被看作没法完成的构造繁琐的构件或部件。” “增材制造技术”更加通俗化的名字叫三维打印。它是一种不依靠模貝,逐级生产制造产品工件的加工工艺。同基本生产工艺流程对比,开发者可以得到更高的可玩性,一旦依靠辅助设计设计方案(CAD)或别的显像加工工艺进行设计产品,便可马上打印。 Pachaly博士及精英团队2014年逐渐下手为有机硅三维打印开发设计系统软件解决方法。他详细介绍说:“三维打印技术现阶段最关键的使用人是机械制造业和航天航空业。增材制造技术日前在医疗行业发展趋势速率更快,微生物模型,依照顾客规定生产制造精准医疗几何图形构件是市场前景尤其宽阔的运用。” 作为产品研发责任人的Pachaly博士注重:“有机硅刚好在这种运用中可以充分运用优点。有机硅不但耐热,还具备超低温柔韧度、微生物兼容模式和清晰度,可以随意上色,消声实际效果也非常优良。” ACEO Imagine Series K可以迅速而高效率地打印样品和小批量生产商品,这类三维打印新技术因而能为工业设计师出示新奇的运用很有可能。 值得一提的是,用以有机硅构件三维打印的增材制造技术已经是业内数月至今的热议话题。因为迄今未有供有机硅应用的完善的三维打印技术,瓦克开发设计的该项加工工艺可以说增材制造技术发展趋势中的里程碑式。 来源于:CPRJ中国塑料硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。