牌号简介 About |
---|
特点:低熔体流动速率均聚聚丙烯具有优异的力学性能和颜色,优异的计量控制和高熔体强度。推荐用途:皮带、片材、纸箱塑料的挤出、挤出热成型、瓶子的挤出吹塑、鞋跟的注射成型、挤出和注射成型的通用应用。 Characteristics: Low melt flow rate Homopolymer polypropylene with excellent mechanical properties and color, excellent gage control and high melt strength. Recommended for: Extrusion of strapping, sheets, Cartonplast, extrusion thermoforming, extrusion blow molding of bottles, injection molding of heels, extrusion and injection molding general purpose applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate 2 |
|||
230℃,2.16kg 230℃,2.16kg 2 |
1.4 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
33.8 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
11 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
1450 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
48 | J/m | ASTM D256-A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 B |
3 类型 1, 2.0 in/min |
4 类型 1, 0.051 in/min |
【新闻资讯】查看全部
大宗商品熊市步伐减缓 三大变数将左右后市行情
2015-11-26 连日跳水的大宗商品市场终于迎来喘息机会:土耳其击落俄罗斯战机,中东地缘局势空前紧张,避险情绪高涨,大宗商品一反惯性下跌而大幅反弹。 盘面看,随着空头大量平仓出局,商品市场看多气氛逐步升温。那么,大宗商品触底了吗?相关人士分析,熊市结束要取决于如下三个变数:一是地缘因素会否发酵,二是熊市逻辑会否动摇,三是避险情绪如何演变。 空头刹车疯熊受挫 受中东地区地缘政治局势紧张影响,隔夜欧美股市下挫,而大宗商品全线上涨, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |