牌号简介 About |
---|
Aristech Acrystics LLC Acrysteel IGP是一种具有溶剂粘合性的连续铸造冲击丙烯酸板。使用0.125”(3.17 mm)厚透明Aristech压克力有限责任公司Acrysteel IGP压克力板测定以下物理性能。属性可能因其他厚度和/或半透明或不透明的颜色而有所不同)。 Aristech Acrylics LLC Acrysteel® IGP is a continuous cast impact acrylic sheet with solvent cementability. The following physical properties were determined using 0.125" (3.17 mm) thickness clear Aristech Acrylics LLC Acrysteel ® IGP acrylic sheet. Properties may vary somewhat on other thicknesses and/or colors translucent or opaque). |
产品描述 Product Description
厂家:美国Aristech
类别:SMMA SMMA
加工条件:热成型 Thermo forming
性能特点: 防火阻燃等级HB; 机械强度好; 耐磨; 硬度高; 可表面喷涂; 耐高温; 可清洁; 冲击性能好; 表面光泽度好; 耐候抗UV; Good Rigidity,Weather resistance is good,Good surface appearance,High impact resistance,Clean,Good Hardness,Sprayable,High Heat Resistance,Good wear resistance,HB
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
平衡,3.17 mm Balance, 3.17 mm |
0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
58 | kJ/m² | ASTM D6110 |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
43 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
4.75 mm 4.75 mm |
21.7 | J | FTMS 406-M-1074 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | 内部方法 | |
热稳定性 thermal stability |
|||
30 minutes @ 180℃ 30 minutes @ 180℃ |
ASTM D4802 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze 3 |
|||
3180 µm 3180 µm 3 |
% | ASTM D1003 | |
黄度指数 Yellowness index |
ASTM D1925 | ||
3.17 mm 3.17 mm |
YI | ASTM D1925 | |
4.75 mm 4.75 mm |
YI | ASTM D1925 | |
5.58 mm 5.58 mm |
YI | ASTM D1925 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热成型温度 Hot forming temperature |
|||
3.17 mm 3.17 mm |
℃ | 内部方法 | |
Odor Odor |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
3.17 mm 3.17 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.17 mm Fracture, 3.17 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23.9°C |
【新闻资讯】查看全部
万华化学与华东理工大学签署战略合作协议
2022-08-31 扫描上图二维码,可以免费下载 搜料 APP 近日,万华化学和华东理工大学战略合作签约仪式在万华化工总部隆重举行。万华化学董事长廖增太、常务副总裁华卫琦、高级副总裁刘博学, |
万华化学与华东理工大学签署战略合作协议 近日,万华化学和华东理工大学战略合作签约仪式在万华化工总部隆重举行。万华化学董事长廖增太、常务副总裁华卫琦、高级副总裁刘博学,华东理工大学校长轩福贞、党委副书记沈海涛、副校长朱为宏、副校长阎海涛等领导出席了签字仪式。这一战略合作协议的签署将把产学研合作提升到一个更高的水平。未来,双方将围绕产业结构和产业发展需要,寻找更多校企合作契合点,期待共同突破行业关键工程技术问题,推动化工行业技术进步、转型升级。
上搜料工程塑料超市www.soliao.com,可以直达现货商城,全部商品都是原厂原包真货,24小时发货,全国含税含运费。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
第三方认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。