牌号简介 About |
---|
HIPLEX TR-130是乙烯和己烯的共聚物,专门为吹塑薄膜生产而设计。非凡的熔融韧性使薄膜厚度降到0.006毫米成为可能。挤出膜具有高的抗冲击性、良好的撕裂强度、优异的防粘连性和良好的阻隔性、低凝胶含量和优异的密封和印刷性能。用途:HIPLEX TR-130适用于广告袋、工业袋、食品包装袋的生产,也适用于复合膜的生产,以及与其他聚乙烯的混合。HIPLEX TR-130具有塞尔维亚卫生防护研究所颁发的健康证书。此外,Hiplex TR-130具有符合性声明,声明产品符合拟接触食品的材料的欧洲规范。符合性声明由斯洛文尼亚Maribor公共卫生研究所发布。 HIPLEX® TR-130, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties. Applications: HIPLEX® TR-130 is suitable for production of advertising bags, industrial bags, bags for food package, and for production of composite films and blends with other kind of polyethylene. HIPLEX® TR-130 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX® TR-130 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.18 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
> 1000 | hr | ASTM D1693B |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm MD, yield, 25 µ m |
24.0 | MPa | ISO 527-3 |
TD,屈服,25 µm TD, yield, 25 µ m |
MPa | ISO 527-3 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
MPa | ISO 527-3 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
断裂 fracture |
% | ISO 527-2 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ISO 527-3 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm 25 µm |
g | ASTM D1709 | |
撕裂强度 tear strength 2 |
ASTM D1922 | ||
MD,25 µm MD,25 µm |
kN/m | ASTM D1922 | |
TD,25 µm TD,25 µm |
kN/m | ASTM D1922 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吹气模制温度 Blowing molding temperature 3 |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服 yield |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
3 Blow-up ratio: 3.5-5 : 1, Neck height: 6-10 times die diameter |
【新闻资讯】查看全部
华美达将于Chinaplas2016展现高速薄壁注塑机最新技术
2016-03-23 ――上海新国际博览中心,2016.4.25-28,展位号:E2M41,敬请莅临参观! 致力于为客户提供更高效、更节能的注塑机产品,华美达塑机将于Chinaplas2016展出用于薄壁制品高速自动化生产及包装的全套解决方案。华美达M8-SPII系列高速薄壁餐盒专用注塑机采取高速低压注射和多动作复合运行设计理念,具有专利设计的多伺服泵组合油路,不仅使开模、储料同时进行(可选开模、顶出动作同步),大幅缩短薄壁制品的生产周期,也大大提升了注塑机的节能效果。经过优化设计的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |