牌号简介 About |
---|
XIRAN® SGH60是基于苯乙烯-马来酸酐(SMA)的注塑成型化合物,具有:高热稳定性、高尺寸稳定性、优异的表面粘合性能。本产品为超黑色(XIRAN® SGH607EB)。应用领域XIRAN® SGH60是一种30%玻璃填充注射成型化合物,设计用于高刚度强度应用。这些产品非常适用于喷涂和发泡零件、耐高温和高丸到丸一致性的精密零件。XIRAN® SGH60适用于底漆聚氨酯涂胶。 XIRAN® SGH60 are styrene maleic anhydride (SMA) based injection molding compounds with: high thermal stability high dimensional stability excellent surface adhesion properties This product is available in extra black (XIRAN® SGH60EB). Application areas XIRAN® SGH60 is a 30% glass filled injection molding compound designed for applications with high stiffness-strength. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency. XIRAN® SGH60 is optimized for primed PU gluing. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
240℃,10.0kg 240℃,10.0kg |
4.0 | g/10min | ISO 1133 |
螺旋流动长度 Spiral flow length 2 |
24.0 | cm | 内部方法 |
收缩率 Shrinkage rate 3 |
|||
TD TD |
0.50 | % | |
MD MD |
0.20 | % | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-40℃ -40℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-40℃ -40℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~80℃ MD:-30~80℃ |
1/℃ | ||
TD:-30~80℃ TD:-30~80℃ |
1/℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
2、模具温度: 65°C, 熔体温度: 250°C, 注塑压力: 70.0 bar |
3、Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
【新闻资讯】查看全部
优库资源方案与大马绿洲公司协作
2018-10-15 优库资源有限公司从传统资源转向再生资源发展,计划与大马绿洲公司合作,在登嘉楼甘�R挽(Kemaman)港口设立再生资源产业园。 对此,优库资源投资总监郑健指出,马来西亚有超过1500家再生塑料颗粒厂,但技术水平落后,而且经营模式有欠规范,亟需整改并进驻规范化再生资源产业园。在塑料原料落实后,大量中国塑料成品工厂也希望产能转移至园区。 “我们与马来西亚绿洲公司合作,打造中马再生资源产业园,发展绿色环保的可持续经济。再生资源是环保产业,节约地球资源,节能减排,无 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |